Process for producing a thiometallate or a selenometallate material

ABSTRACT

A method for producing a thiometallate or selenometallate material is provided in which a first salt containing an anionic component selected from the group consisting of MoS 4   2− , MoSe 4   2− , WS 4   2− , WSe 4   2− , VS 4   3− , and VSe 4   3− , and a second salt containing a cationic component comprising a metal in any non-zero oxidation state selected from the group consisting of Fe, Ag, Co, Mn, Re, Ru, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn, Pb, Cd, Sb, Ge, Ga, In, Au, Hg are mixed under anaerobic conditions in an aqueous mixture at a temperature of from 15° C. to 150° C.

CROSS REFERENCE TO RELATED APPLICATION

The present application claims the benefit of priority from U.S. Provisional Patent Application Ser. No. 61/297,084 filed Jan. 21, 2010.

FIELD OF THE INVENTION

The present invention is directed to a process for producing a thiometallate or selenometallate material. In particular, the present invention is directed to a process for producing a bimetallic or polymetallic thiometallate or selenometallate material.

BACKGROUND OF THE INVENTION

Increasingly, resources such as heavy crude oils, tar sands, shale oils, and coal are being utilized as hydrocarbon sources due to decreasing availability of easily accessed light sweet crude oil reservoirs. These resources are disadvantaged relative to light sweet crude oils, often containing significant amounts of sulfur, nitrogen, metals, and heavy hydrocarbon fractions including residue and asphaltenes. The disadvantaged crudes typically require a considerable amount of upgrading in order to obtain useful hydrocarbon products therefrom.

Numerous catalysts have been developed for catalytically hydrocracking and hydrotreating disadvantaged hydrocarbon feedstocks. Typically, these catalysts contain a Group VIB or Group VIII metal supported on a carrier formed of alumina, silica, or alumina-silica. Such catalysts are commonly sulfided to activate the catalyst, either before contacting the catalyst with a disadvantaged hydrocarbon feed or in situ with the disadvantaged hydrocarbon feed.

Applicants have discovered that a bimetallic or polymetallic thiometallate or selenometallate material is an exceptionally good catalyst for upgrading disadvantaged hydrocarbon feedstocks, particularly for converting all or substantially all heavy fractions such as residue and asphaltenes in the feedstock to lighter fractions while forming little or no coke. In particular, Applicants have discovered that bimetallic tetrathiomolybdates, tetrathiotungstates, and tetrathiovanadates and/or polymetallic tetrathiomolybdates, tetrathiotungstates, and tetrathiovanadates, and their tetraseleno-analogs are especially effective for hydrocracking disadvantaged hydrocarbon feedstocks to upgrade the feedstocks.

Ammonium and alkylammonium thiometallates have been used as precursors to produce metal sulfides. For example, tetralkylammonium thiomolybdate, tetralkylammonium thiotungstate, and ammonium thiomolybdate precursor compounds have been treated at temperatures of above 350° C. to thermally decompose the precursor compounds to produce MoS₂ and WS₂ disulfides having predicable stoichoimetry that have a high surface area and show substantial hydrodesulfurization and hydrodenitrogenation catalytic activity. Ammonium thiometallates have also been used as precursors to produce bimetallic compounds in an organic solvent. For example, copper thiometallates and copper selenometallates have been produced using a solvothermal method by reacting (NH₄)₂MoS₄, (NH₄)₂WS₄, (PPh₄)₂MoSe₄, or (PPh₄)₂WSe₄ with copper borofluoride salts in organic solvents at temperatures of 110° C. or above in an autoclave at autogenous pressures. Iron-molybdenum sulfide compounds have been produced by dissolving (NH₄)₂MoS₄ in an organic chelating solution of diethylenetriamine (dien) and slowly adding an iron salt in a 10% aqueous dien solution to precipitate a hydrodenitrogenation catalyst precursor. The precursor is thermally decomposed to remove organic ligand constituents and sulfactivate the catalyst. Such methods may be impractical for producing high yields of bimetallic or polymetallic thiometallates having a high surface area in a cost effective manner due to the temperatures, pressures, and solvents required, or due to the nature of the products themselves.

A method of preparing copper tetrathiomolybdates from ammonium tetrathiomolybdates and a copper salt is described in The Copper-Molybdenum Antagonism in Ruminants. III. Reaction of Copper(II) with Tetrathiomolybdate(VI), Laurie, Pratt, & Raynor, Inorganica Chimica Acta, 123 (1986) 193-196. Aqueous solutions of reactants CuSO₄.5H₂O and M₂ ^(I)-MoS₄ (M^(I)=NH₄ ⁺, Et₄N⁺, or Na⁺) and (NH₄)₂MoS₄ were mixed to form a solid product which was collected by filtration, washed, and then dried. The solid product contained two materials, a composition M^(I)CuMoS₄ (where M^(I) is the M^(I) included in the tetrathiomolybdate reactant) and a composition CuMoS_(4-x)O_(x), where x=2 or 3.

Improved processes are desirable for producing non-copper thiometallate or selenometallate materials, particularly bimetallic or polymetallic thiometallate or selenometallate materials.

SUMMARY OF THE INVENTION

The present invention is directed to a method for producing a thiometallate or selenometallate material, comprising:

mixing a first salt and a second salt in an aqueous mixture under anaerobic conditions, where, during mixing the aqueous mixture has a temperature of from 15° C. to 150° C., and wherein the first salt comprises a cationic component containing one or more metals selected from the group consisting of an alkali metal, an alkaline earth metal, and mixtures thereof and comprises an anionic component containing a first metal selected from the group consisting of Mo, W, and V where the anionic component is selected from the group consisting of MoS₄ ²⁻, MoSe₄ ²⁻, WS₄ ²⁻, WSe₄ ²⁻, VS₄ ³⁻, and VSe₄ ³⁻ and mixtures thereof, and wherein the second salt comprises a cationic component comprising a second metal in any non-zero oxidation state selected from the group consisting of Fe, Ag, Co, Mn, Re, Ru, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn and mixtures thereof, where the first and second salts are soluble in the aqueous mixture;

separating a solid material from the aqueous mixture comprising a) the first metal; and b) the second metal, wherein at least a portion of the solid material separated from the aqueous mixture has a structure according to a formula selected from the group consisting of formula (I), formula (II), formula (III), and formula (IV):

where M is either the first metal or the second metal; at least one M is the first metal and at least one M is the second metal; and Q is either sulfur or selenium;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is directed to a method for producing a thiometallate or a selenometallate material, in particular, a tetrathiometallate or a tetraselenometallate material. The method is conducted in an aqueous solution at low temperatures compared to thermal solvolysis methods, which typically are effected at temperatures above 150° C. As such, bulk quantities of the thiometallate or selenometallate materials may be easily produced at relatively low cost. The method produces a polymeric tetrathiometallate or tetraselenometallate material that is substantially free of oxygen contaminants and contaminants derived from tetrathio- or tetraselenometallate salt counterions such as ammonium, sodium, or potassium. The method is also effective to produce significant quantities of the polymeric tetrathiometallate or tetraselenometallate material as small or nano particles having a large surface area that are effective as a catalyst for hydrocracking a heavy hydrocarbon feedstock.

As used herein, the phrase “anaerobic conditions” means “conditions in which less than 0.5 vol. % oxygen gas is present”. For example, a process that occurs under anaerobic conditions, as used herein, is a process that occurs in the presence of less than 0.5 vol. % oxygen gas. Anaerobic conditions may be such that no detectable oxygen gas is present.

“ASTM” as used herein refers to American Standard Testing Method.

The term “aqueous” as used herein is defined as containing more than 50 vol. % water. For example, an aqueous solution or aqueous mixture, as used herein, contains more than 50 vol. % water.

The term “dispersible” as used herein with respect to mixing a solid, such as a salt, in a liquid is defined to mean that the components that form the solid, upon being mixed with the liquid, are retained in the liquid for a period of at least 24 hours upon cessation of mixing the solid with the liquid. A solid material is dispersible in a liquid if the solid or its components are soluble in the liquid. A solid material is also dispersible in a liquid if the solid or its components form a colloidal dispersion or a suspension in the liquid.

The term “ligand” as used herein is defined as a molecule or ion attached to, or capable of attaching to, a metal ion in a coordination complex.

The term “monomer” as used herein is defined as a molecular compound that may be reactively joined with itself or another monomer in repeated linked units to form a polymer.

The term “polymer” as used herein is defined herein as a compound comprised of repeated linked monomer units.

As used herein, an element of the Periodic Table of Elements may be referred to by its symbol in the Periodic Table. For example, Cu may be used to refer to copper, Au may be used to refer to gold, Hg may be used to refer to mercury etc.

The term “soluble” as used herein refers to a substance a majority (e.g. greater than 50 wt. %) of which dissolves in a liquid upon being mixed with the liquid at a specified temperature and pressure. For example, a material dispersed in a liquid is soluble in the liquid if less than 50 wt. % of the material may be recovered from the liquid by centrifugation and filtration.

In the process of the present invention, a first salt comprised of an anionic component containing a first metal selected from the group consisting of Mo, W, and V and a second salt comprised of a cationic component containing a metal are mixed in an aqueous mixture under anaerobic conditions at a temperature of from 15° C. to 150° C., and a solid material is separated from the aqueous mixture where the separated solid material contains a) the first metal of the anionic component of the first salt; and b) the second metal of the cationic component of the second salt, wherein at least a portion of the solid material separated from the aqueous mixture has a structure according to a formula selected from the group consisting of formula (I), formula (II), formula (III), and formula (IV);

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, and Q is either sulfur or selenium;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃.

The first salt utilized in the process of the present invention includes an anionic component that is a tetrathiometallate or a tetraselenometallate, where the metal of the anionic component of the first salt is selected from the group consisting of molybdenum, tungsten, and vanadium and is defined herein as the first metal. In particular, the first salt contains an anionic component that is selected from the group consisting of MoS₄ ²⁻, MoSe₄ ²⁻, WS₄ ²⁻, WSe₄ ²⁻, VS₄ ³⁻, and VSe₄ ³⁻.

The first salt also contains a cationic component associated with the anionic component of the first salt to form the first salt. The cationic component of the first salt may be selected from alkali metal and alkaline earth metal counterions to the tetrathiometallate or the tetraselenometallate anionic component of the first salt so long as the combined cationic component and the anionic component of the first salt form a salt that is dispersable, and preferably soluble, in the aqueous mixture in which the first salt and the second salt are mixed, and so long as the cationic component of the first salt does not prevent the combination of the anionic component of the first salt with the cationic component of the second salt in the aqueous mixture to form the solid product material. Preferably, the cationic component balances the charge of the anionic component in the first salt. In a preferred embodiment, the cationic component of the first salt comprises one or more sodium ions, or one or more potassium ions.

Certain compounds are preferred for use as the first salt in the process of the present invention. In particular, the first salt is preferably selected from the group consisting of Na₂MoS₄, Na₂WS₄, Na₃VS₄, K₂MoS₄, K₂WS₄, K₃VS₄, Na₂MoSe₄, Na₂WSe₄, K₂MoSe₄, K₂WSe₄, K₃VSe₄, K₃WSe₄ and hydrates thereof.

The first salt may be produced from a commercially available tetrathiomolybdate, tetrathiotungstate, or tetrathiovanadate salt. For example, the first salt may be produced from ammonium tetrathiomolybdate, ammonium tetrathiotungstate, or from ammonium tetrathiovanadate. The first salt may be formed from the commercially available ammonium tetrathiometallate salts by exchanging the cationic ammonium component of the commercially available salt with a desired alkali or alkaline earth cationic component from a separate salt. The exchange of the cationic components to form the desired first salt may be effected by mixing the commercially available salt and the salt containing the desired cationic component in an aqueous solution to form the desired first salt.

A method of forming the first salt is to disperse an ammonium tetrathiomolybdate, ammonium tetrathiotungstate, or ammonium tetrathiovanadate salt in an aqueous solution, preferably water, and to disperse an alkali metal or alkaline earth metal cationic component donor salt, preferably a carbonate, in the aqueous solution, where the cationic component donor salt is provided in an amount relative to the ammonium tetrathiomolybdate, ammonium tetrathiotungstate, or ammonium tetrathiovanadate salt to provide a stoichiometrially equivalent or greater amount of its cation to ammonium of the ammonium tetrathiomolybdate, ammonium tetrathiotungstate, or ammonium tetrathiovanadate salt. The aqueous solution may be heated to a temperature of at least 50° C., or at least 65° C. up to 100° C. to evolve ammonia from the ammonium containing salt and carbon dioxide from the carbonate containing salt as gases, and to form the second salt. For example a Na₂MoS₄ salt may be prepared for use as the first salt by mixing commercially available (NH₄)₂MoS₄ and Na₂CO₃ in water at a temperature of 70° C.-80° C. for a time period sufficient to permit evolution of a significant amount, preferably substantially all, of ammonia and carbon dioxide gases from the solution, typically from 30 minutes to 4 hours, and usually about 2 hours.

The first salt may be contained in an aqueous solution or an aqueous mixture, where, in the process of the present invention, the aqueous solution or aqueous mixture containing the first salt (hereinafter the “first aqueous solution”) may be mixed with the second salt or an aqueous solution containing the second salt (hereinafter the “second aqueous solution”) in the aqueous mixture to form the solid product material. The first salt is preferably dispersible, and most preferably soluble, in the first aqueous solution and is dispersible, and preferably soluble, in the aqueous mixture of the first and second salts. The first aqueous solution contains more than 50 vol. % water, or at least 75 vol. % water, or at least 90 vol. % water, or at least 95 vol. % water, and may contain more than 0 vol. % but less than 50 vol. %, or at most 25 vol. %, or at most 10 vol. %, or at most 5 vol. % of an organic solvent containing from 1 to 5 carbons selected from the group consisting of an alcohol, a diol, an aldehyde, a ketone, an amine, an amide, a furan, an ether, acetonitrile, and mixtures thereof. The organic solvent present in the first aqueous solution, if any, should be selected so that the organic compounds in the organic solvent do not inhibit reaction of the anionic component of the first salt with the cationic component of the second salt upon forming an aqueous mixture containing the first aqueous solution, e.g., by forming ligands or by reacting with the first or second salts or their respective cationic or anionic components. Preferably, the first aqueous solution contains no organic solvent. Most preferably the first aqueous solution consists essentially of water, most preferably deionized water, and the first salt, although in a less preferred embodiment the first aqueous solution may contain compounds other than the first salt, such as a buffer compound.

If the first salt is contained in a first aqueous solution, the concentration of the first salt in the first aqueous solution may be selected to promote formation of a solid product material having a particle size distribution with a small mean and/or median particle size and having a relatively large surface area per particle upon mixing the first salt and the second salt in the aqueous mixture. It has been found that decreasing the instantaneous concentration of the first salt and/or the second salt during mixing in the aqueous mixture produces a solid product material comprised of smaller particles relative to solid product materials produced from an aqueous mixture containing higher instantaneous concentrations of the first and second salts, where the small particles have a relatively large surface area. In an embodiment of the process of the invention, the first aqueous solution may contain at most 0.8 moles per liter, or at most 0.6 moles per liter, or at most 0.4 moles per liter, or at most 0.2 moles per liter, or at most 0.1 moles per liter of the first salt.

The second salt utilized in the process of the present invention includes a cationic component comprising a metal in any non-zero oxidation state selected from the group consisting of Fe, Ag, Co, Mn, Re, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn, Pb, Cd, Sb, Ge, Ga, In, Au, Hg, and mixtures thereof, defined herein as the second metal. The cationic component of the second salt contains at most 1 part per million of copper, and preferably contains no copper. The cationic component of the second salt may consist essentially of a metal selected from the group consisting of Fe, Ag, Co, Mn, Re, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn, Pb, Cd, Sb, Ge, Ga, In, Au, Hg, and mixtures thereof. The cationic component of the second salt must be capable of bonding with the anionic component of the first salt to form the solid product material in the aqueous mixture at a temperature of from 15° C. to 150° C. and under anaerobic conditions.

The second salt also contains an anionic component associated with the cationic component of the second salt to form the second salt. The anionic component of the second salt may be selected from a wide range of counterions to the cationic component of the second salt so long as the combined cationic component and the anionic component of the second salt form a salt that is dispersible, and preferably soluble, in the aqueous mixture in which the first salt and the second salt are mixed, and so long as the anionic component of the second salt does not prevent the combination of the anionic component of the first salt with the cationic component of the second salt in the aqueous mixture to form the solid product material. Preferably, the anionic component of the second salt balances the charge of the cationic component of the second salt in the second salt. The anionic component of the second salt may be selected from the group consisting of sulfate, chloride, bromide, iodide, acetate, acetylacetonate, phosphate, nitrate, perchlorate, oxalate, citrate, and tartrate.

Certain compounds are preferred for use as the second salt to produce the tetrathiometallate or tetraselenometallate material of the present invention. In particular, the second salt is preferably selected from the group consisting of FeSO₄, Fe(NO₃)₂, Fe(NO₃)₃, FeCl₂, FeCl₃, iron acetate, iron acetylacetonate, FeBr₂, Fe(ClO₄)₂, Fe(ClO₄)₃, ferric citrate, NiSO₄, nickel acetate, nickel acetylacetonate, NiCl₂, Ni(NO₃)₂, Ni(ClO₄)₂, Ni(ClO₃)₂, CoSO₄, CoCl₂, cobalt acetate, cobalt acetylacetonate, Co(NO₃)₂, Co(ClO₄)₂, CoI₂, CoBr₂, Co(ClO₃)₂, ZnCl₂, ZnSO₄, zinc acetate, zinc acetylacetonate, ZnBr₂, ZnI₂, Zn(NO₃)₂, Zn(ClO₃)₂, Zn(ClO₄)₂, silver acetate, silver acetylacetonate, AgClO₃, AgClO₄, AgNO₃, SnSO₄, SnCl₂, tin acetate, tin acetylacetonate, SnBr₂, Bi₂(SO₄)₃, BiCl₃, bismuth acetate, bismuth acetylacetonate, and hydrates and mixtures thereof. These materials are generally commercially available, or may be prepared from commercially available materials according to well-known methods.

The second salt may be contained in an aqueous solution (the second aqueous solution, as noted above), where, in the process of the present invention, the second aqueous solution containing the second salt may be mixed with the first salt or a first aqueous solution containing the first salt in the aqueous mixture to form the solid product material. The second salt is preferably dispersible, and most preferably soluble, in the second aqueous solution and is dispersible, and preferably soluble, in the aqueous mixture containing the first and second salts. The second aqueous solution contains more than 50 vol. % water, or at least 75 vol. % water, or at least 90 vol. % water, or at least 95 vol. % water, and may contain more than 0 vol. % but less than 50 vol. %, or at most 25 vol. %, or at most 10 vol. %, or at most 5 vol. % of an organic solvent containing from 1 to 5 carbons and selected from the group consisting of an alcohol, a diol, an aldehyde, a ketone, an amine, an amide, a furan, an ether, acetonitrile, and mixtures thereof. The organic solvent present in the second aqueous solution, if any, should be selected so that the organic compounds in the organic solvent do not inhibit reaction of the anionic component of the first salt with the cationic component of the second salt upon forming an aqueous mixture containing the second aqueous solution, e.g., by forming ligands or by reacting with the first or second salts or their respective cationic or anionic components. Preferably, the second aqueous solution contains no organic solvent. Most preferably the second aqueous solution consists essentially of water, preferably deionized, and the second salt, although in a less preferred embodiment the second aqueous solution may contain compounds other than the second salt, such as a buffer.

If the second salt is contained in a second aqueous solution, the concentration of the second salt in the second aqueous solution may be selected to promote formation of a solid product material having a particle size distribution with a small mean and/or median particle size, where the particles have a relatively large surface area, upon mixing the first salt and the second salt in the aqueous mixture. As noted above, it has been found that decreasing the instantaneous concentration of the first salt and/or the second salt during mixing in the aqueous mixture produces a solid product material comprised of smaller particles relative to solid product materials produced from an aqueous mixture containing higher instantaneous concentrations of the first and second salts. In an embodiment of the process of the invention, the second aqueous solution may contain at most 3 moles per liter, or at most 2 moles per liter, or at most 1 mole per liter, or at most 0.6 moles per liter, or at most 0.2 moles per liter of the second salt.

In the process of the present invention, the first salt and the second salt are mixed in an aqueous mixture to form the solid product material. The amount of the first salt relative to the amount of the second salt provided to the aqueous mixture may be selected so that the atomic ratio of the second metal of the second salt to the first metal of the anionic component of the first salt, either molybdenum, tungsten, or vanandium, is from 2:3 to 20:1, or from 1:1 to 10:1. The amount of the first salt and the second salt provided to the aqueous mixture may be selected so that the atomic ratio of the second metal of the second salt to the first metal of the anionic component of the first salt is at least 1.5:1, or at least 1.6:1, or at least 2:1, or more than 2:1 since selection of a ratio of less than 1.5:1 may lead to incorporation of a small quantity of the cationic component of the first salt in the solid material product.

In one embodiment, an aqueous mixture of the first salt and the second salt may be formed by adding a solid form of the second salt to an aqueous solution containing the first salt (the first aqueous solution). Alternatively, the aqueous mixture of the first salt and the second salt may be formed by adding a solid form of the first salt to an aqueous solution containing the second salt (the second aqueous solution). In a further embodiment, the aqueous mixture of the first and second salts may be formed by combining a first aqueous solution containing the first salt and a second aqueous solution containing the second salt. If desired, water—preferably deionized—may be added to the aqueous mixture formed by any of these methods to dilute the aqueous mixture and reduce the concentrations of the first and second salts in the aqueous mixture.

In another embodiment of the process of the present invention, the aqueous mixture of the first and second salts may be formed by adding the first salt and the second salt into an aqueous solution separate from both a first aqueous solution containing the first salt and a second aqueous solution containing the second salt. The separate aqueous solution will be referred hereafter as the “third aqueous solution”. The third aqueous solution, if utilized, contains more than 50 vol. % water, or at least 75 vol. % water, or at least 90 vol. % water, or at least 95 vol. % water, and may contain more than 0 vol. % but less than 50 vol. %, or at most 25 vol. %, or at most 10 vol. %, or at most 5 vol. % of an organic solvent containing from 1 to 5 carbons and selected from the group consisting of an alcohol, a diol, an aldehyde, a ketone, an amine, an amide, a furan, an ether, acetonitrile, and mixtures thereof. The organic solvent present in the third aqueous solution, if any, should be selected so that the organic compounds in the organic solvent do not inhibit reaction of the anionic component of the first salt with the cationic component of the second salt upon forming the aqueous mixture, e.g., by forming ligands or reacting with the anionic component of the first salt or with the cationic component of the second salt. Preferably, the third aqueous solution contains no organic solvent, and most preferably comprises deionized water.

In an embodiment of the process of the present invention, the first salt and the second salt may be added as solids to the third aqueous solution. Alternatively, either the first salt in a first aqueous solution or the second salt in a second aqueous solution may be added to the third aqueous solution while adding the other salt in solid form to form the aqueous mixture. If desired, water may be added to the aqueous mixture formed by any of these methods to dilute the aqueous mixture and reduce the concentrations of the first and second salts in the aqueous mixture.

In a preferred embodiment of the process of the present invention, the aqueous mixture of the first and second salts may be formed by combining a first aqueous solution containing the first salt and a second aqueous solution containing the second salt in a third aqueous solution. The volume ratio of the third aqueous solution to the first aqueous solution containing the first salt may be from 0.5:1 to 50:1 where the first aqueous solution preferably contains at most 0.8, or at most 0.4, or at most 0.2, or at most 0.1 moles of the first salt per liter of the first aqueous solution. Likewise, the volume ratio of the third aqueous solution to the second aqueous solution containing the second salt may be from 0.5:1 to 50:1 where the second aqueous solution preferably contains at most 3, or at most 2, or at most 1, or at most 0.8, or at most 0.5, or at most 0.3 moles of the second salt per liter of the second aqueous solution.

The first salt and the second salt may be combined in the aqueous mixture, regardless of which method is selected to combine the first and second salts, so that the aqueous mixture containing the first and second salts contains at most 1.5, or at most 1.2, or at most 1, or at most 0.8, or at most 0.6 moles of the combined first and second salts per liter of the aqueous mixture. It has been found that particle size of the solid material product produced by mixing the first and second salts in the aqueous mixture increases and the surface area of the particles decreases with increasing concentrations of the salts. Therefore, to limit the particle sizes in the particle size distribution of the solid material product and to increase the relative surface area of the particles, the aqueous mixture may contain at most 0.8 moles of the combined first and second salts per liter of the aqueous mixture, more preferably at most 0.6 moles, or at most 0.4 moles, or at most 0.2 moles of the combined first and second salts per liter of the aqueous mixture. The amount of first salt and the total volume of the aqueous mixture may be selected to provide at most 0.4, or at most 0.2, or at most 0.1, or at most 0.01 moles of the anionic component per liter of the aqueous mixture, and the amount of the second salt and the total volume of the aqueous mixture may be selected to provide at most 1, or at most 0.8, or at most 0.4 moles of the cationic component per liter of the aqueous mixture.

The rate of addition of the first salt and/or the second salt to the aqueous mixture may be controlled to limit the instantaneous concentration of the first salt and/or the second salt in the aqueous mixture to produce a solid product material comprised of relatively small particles having relatively large surface area. Limiting the instantaneous concentration of one or both salts in the aqueous mixture may reduce the mean and/or median particle size of the resulting solid product material by limiting the simultaneous availability of large quantities of the anionic components of the first salt and large quantities of the cationic components of the second salt that may interact to form a solid product material comprised primarily of relatively large particles. In an embodiment of the process of the present invention, the rate of addition of the first salt and/or the second salt to the aqueous mixture is controlled to limit the instantaneous concentration of the first salt and/or the second salt in the aqueous mixture to at most 0.05 moles per liter, or at most 0.01 moles per liter, or at most 0.001 moles per liter.

The rate of addition of the first salt and/or the second salt to the aqueous mixture may be controlled by limiting the rate of addition of a first aqueous solution containing the first salt and/or the rate of addition of a second aqueous solution containing the second salt to the aqueous mixture. In one embodiment of the process of the present invention, the first aqueous solution containing the first salt may be added to the second aqueous solution containing the second salt, or the second aqueous solution may be added to the first aqueous solution, where the solution being added is added in a dropwise manner to the other solution. The rate of addition of drops of the first aqueous solution to the second aqueous solution or of drops of the second aqueous solution to the first aqueous solution may be controlled to provide the desired instantaneous concentration of the first salt or of the second salt in the aqueous mixture. In another embodiment, the first aqueous solution containing the first salt may be dispersed directly into the second aqueous solution containing the second salt at a controlled flow rate to provide a desired instantaneous concentration of the first salt in the aqueous mixture. Alternatively, the second aqueous solution containing the second salt may be dispersed directly into the first aqueous solution containing the first salt at a controlled flow rate selected to provide a desired instantaneous concentration of the second salt in the aqueous mixture. The first aqueous solution may be directly dispersed into the second aqueous solution or the second aqueous solution may be directly dispersed into the first aqueous solution at a selected controlled flow rate using conventional means for dispersing one solution into another solution at a controlled flow rate. For example, one solution may dispersed through a nozzle located in the other solution, where the flow of the solution through the nozzle may be metered by a flow rate control device.

In a preferred embodiment, the first aqueous solution containing the first salt and the second aqueous solution containing the second salt are added to a third aqueous solution, preferably simultaneously, at a controlled rate selected to provide a desired instantaneous concentration of the first salt and the second salt in the aqueous mixture. The first aqueous solution containing the first salt and the second aqueous solution containing the second salt may be added to the third aqueous solution at a controlled rate by adding the first aqueous solution and the second aqueous solution to the third aqueous solution in a dropwise manner. The rate that drops of the first aqueous solution and the second aqueous solution are added to the third aqueous solution may be controlled to limit the instantaneous concentration of the first salt and the second salt in the aqueous mixture as desired. In a preferred embodiment, the first aqueous solution containing the first salt and the second aqueous solution containing the second salt are dispersed directly into the third aqueous solution at a flow rate selected to provide a desired instantaneous concentration of the first salt and the second salt. The first aqueous solution and the second aqueous solution may be dispersed directly into the third aqueous solution using conventional means for dispersing one solution into another solution at a controlled flow rate. For example, the first aqueous solution and the second aqueous solution may be dispersed into the third aqueous solution by pumping the respective solutions through separate nozzles located within the third aqueous solution, where the flow of the first and second solutions through the nozzles is metered by separate flow metering devices.

The particle size distribution of the solid material produced by mixing the first salt and the second salt in the aqueous mixture is preferably controlled by the rate of addition of the first salt and/or the second salt to the aqueous mixture, as described above, so that the median and/or mean particle size of the particle size distribution falls within a range of from 50 nm to 50 μm. In a preferred embodiment, the particle size distribution of the solid material is controlled by the rate of addition of the first and/or second salts to the aqueous mixture so that the median and/or mean particle size of the particle size distribution of the solid material may range from at least 50 nm up to 5 μm, or up to 1 μm, or up to 750 nm.

The surface area of the solid material particles produced by mixing the first salt and the second salt in the aqueous mixture is also preferably controlled by the rate of addition of the first salt and/or the second salt to the aqueous mixture, as described above, so that the BET surface area of the solid material particles is from 50 m²/g to 500 m²/g. In an embodiment, the surface area of the solid material particles is controlled by the rate of addition of the first salt and/or the second salt to the aqueous mixture so that the BET surface area of the solid material particles is from 100 m²/g to 350 m²/g

The aqueous mixture contains more than 50 vol. % water, or at least 75 vol. % water, or at least 90 vol. % water, or at least 95 vol. % water, and may contain more than 0 vol. % but less than 50 vol. %, or at most 25 vol. %, or at most 10 vol. %, or at most 5 vol. % of an organic solvent containing from 1 to 5 carbons and selected from the group consisting of an alcohol, a diol, an aldehyde, a ketone, an amine, an amide, a furan, an ether, acetonitrile, and mixtures thereof. The organic solvent present in the aqueous mixture, if any, should not inhibit reaction of the anionic component of the first salt with the cationic component of the second salt. Preferably, the aqueous mixture contains no organic solvent.

The aqueous mixture containing the first salt and the second salt is mixed to facilitate interaction and reaction of the anionic component of the first salt with the cationic component of the second salt to form the solid product material. The aqueous mixture may be mixed by any conventional means for agitating a solution, for example by mechanical stirring.

During mixing, the temperature of the aqueous mixture is maintained in the range of from 15° C. to 150° C., or from 60° C. to 125° C., or most preferably from 65° C. to 100° C. In a preferred embodiment of the process of the present invention, the temperature of the aqueous mixture during mixing is maintained at less than 100° C. so that the mixing may be conducted without the application of positive pressure necessary to inhibit the water in the aqueous mixture from becoming steam.

Maintaining the temperature of the aqueous mixture in a range of from 50° C. to 150° C. may result in production of a solid material having a relatively large surface area and a substantially reduced median or mean particle size relative to a solid material produced in the same manner at a lower temperature. It is believed that maintaining the temperature in the range of 50° C. to 150° C. drives the reaction of the cationic component of the second salt with the anionic component of the first salt, reducing the reaction time and limiting the time available for the resulting product to agglomerate prior to precipitation. Maintaining the temperature in a range of from 50° C. to 150° C. during the mixing of the first and second salts in the aqueous mixture may result in production of a solid material having a particle size distribution with a median or mean particle size of from 50 nm up to 5 μm, or up to 1 μm, or up to 750 nm; and having a BET surface area of from 50 m²/g up to 500 m²/g or from 100 m²/g to 350 m²/g.

The aqueous mixture may be heated using any conventional means for heating a solution being mixed. For example, the aqueous mixture may be mixed in a jacketed mixing apparatus, where heat may be applied to the aqueous mixture by passing steam through the jacket of the mixing apparatus. If utilized, the first aqueous solution, second aqueous solution, and/or the third aqueous solution may be heated to a temperature within the desired range prior to forming the aqueous mixture by mixing the first and second salts.

The first and second salts in the aqueous mixture may be mixed under a pressure of from 0.101 MPa to 10 MPa (1.01 bar to 100 bar). Preferably, the first and second salts in the aqueous mixture are mixed at atmospheric pressure, however, if the mixing is effected at a temperature greater than 100° C. the mixing may be conducted under positive pressure to inhibit the formation of steam.

During mixing, the aqueous mixture is maintained under anaerobic conditions. Maintaining the aqueous mixture under anaerobic conditions during mixing inhibits the oxidation of the solid product material or the anionic component of the first salt so that the solid material product produced by the process contains little, if any oxygen. It is believed that exclusion of oxygen from the solid material increases the crystallinity of the solid material—if the aqueous mixture is mixed in the presence of significant quantities of oxygen the resulting product is an amorphous mass that is not useful as a catalyst for upgrading a heavy crude oil. The aqueous mixture may be maintained under anaerobic conditions during mixing by conducting the mixing in an atmosphere containing little or no oxygen, preferably an inert atmosphere. The mixing of the first and second salts in the aqueous mixture may be conducted under nitrogen, argon, and/or steam to maintain anaerobic conditions during the mixing. In a preferred embodiment of the process of the present invention, an inert gas, preferably nitrogen or steam, is continuously injected into the aqueous mixture during mixing to maintain anaerobic conditions and to facilitate mixing of the first and second salts in the aqueous mixture.

The first and second salts are mixed in the aqueous mixture at a temperature of from 15° C. to 150° C. under anaerobic conditions for a period of time sufficient to permit the formation of solid material product comprised of a plurality of anionic components from the first salt and a plurality of cationic components from the second salt. The first and second salt may be mixed in the aqueous mixture for a period of at least 1 hour, or at least 2 hours, or at least 3 hours, or at least 4 hours, or from 1 hour to 10 hours, or from 2 hours to 9 hours, or from 3 hours to 8 hours, or from 4 hours to 7 hours to permit the formation of the solid material product. In an embodiment of the process of the invention, the first and/or second salt(s) may be added to the aqueous mixture over a period of from 30 minutes to 4 hours while mixing the aqueous mixture, and after the entirety of the first and second salts have been mixed into the aqueous mixture, the aqueous mixture may be mixed for at least an additional 1 hour, or 2 hours, or 3 hours or 4 hours, or 5 hours to permit the formation of the solid material product.

After completing mixing of the aqueous mixture of the first and second salts, a solid material is separated from the aqueous mixture. The solid may be separated from the aqueous mixture by any conventional means for separating a solid phase material from a liquid phase material. For example, the solid may be separated by allowing the solid to settle from the resulting mixture, preferably for a period of from 1 hour to 16 hours, and separating the solid from the mixture by vacuum or gravitational filtration or by centrifugation. To enhance recovery of the solid, water may be added to the aqueous mixture prior to allowing the solid to settle. In an embodiment, water may be added to the aqueous mixture in a volume relative to the volume of the aqueous mixture of from 0.1:1 to 0.75:1. Alternatively, but less preferably, the solid may be separated from the mixture by centrifugation without first allowing the solid to settle and/or without the addition of water. The solid material may also be separated from the aqueous mixture by spray drying the aqueous mixture.

The separated solid material product may be washed subsequent to separating the solid material from the aqueous mixture, if desired. The separated solid material may be contaminated with minor amounts, typically less than 0.5 wt. %, of the cationic component from the first salt and/or the anionic component from the second salt. These minor contaminants may be removed from the separated solid material by washing the separated solid material with water. Substantial volumes of water may be used to wash the separated solid material since the separated solid material is insoluble in water, and the yield of solid material product will not be significantly affected by the wash.

The optionally washed separated solid material product may be dried, if desired. The separated solid material product may be dried by heating the solid material and/or by holding the solid material under vacuum. The solid material may be dried by heating to a temperature of from 35° C. to 75° C. under anaerobic conditions for a period of time sufficient to dry the solid material, typically from 12 hours to 5 days. The solid material may be dried by vacuum by holding the solid material under a vacuum for a period of from 12 hours to 5 days. Preferably the solid material is dried by heating to a temperature of from 35° C. to 75° C. under vacuum for a period of 2 to 4 days.

The solid material may be produced from the first and second salts in relatively good yield. The solid material may be produced at a molar yield of at least 45% up to 95%, or up to 90%, or up to 85% from the first and second salts.

The solid material separated from the aqueous mixture, optionally washed and/or optionally dried, is comprised of a) the first metal of the anionic component of the first salt; and b) the second metal of the cationic component of the second salt, wherein at least a portion of the solid material separated from the aqueous mixture has a structure according to a formula selected from the group consisting of formula (I), formula (II), formula (III), and formula (IV);

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, and Q is either sulfur or selenium;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃.

The solid material separated from the aqueous mixture may be comprised of a plurality of anionic components of the first salt and a plurality of cationic components from the second salt in which anionic components from the first salt in the solid material are bonded with at least a portion of the cationic components from the second salt in the solid material in two or more repeating units. The solid material may be comprised of alternating atoms of the first metal of the anionic component of the first salt and the second metal of the cationic component of the second salt bonded to and linked by two sulfur atoms. The solid material may comprise alternating M¹S₄ and M²S₄ tetrahedral formations, where each tetrahedral formation shares at least two sulfur atoms with an adjacent tetrahedral formation, where M¹ is the first metal of the anionic component of the first salt and M² is the second metal of the cationic component of the second salt. The solid material may be comprised of alternating atoms of the first metal of the anionic component of the first salt and the second metal of the cationic component of the second salt bonded to an linked to and linked by two selenium atoms. The solid material may comprise alternating M¹Se₄ and M²Se₄ tetrahedral formations, where each tetrahedral formation shares at least two selenium atoms with an adjacent tetrahedral formation, where M¹ is the first metal of the anionic component of the first salt and M² is the second metal of the cationic component of the second salt.

In an embodiment of the present invention, the solid material separated from the aqueous mixture is comprised of the first metal of the anionic component of the first salt and the second metal of the cationic component of the second salt, where the solid material is comprised of at least three linked chain elements, the chain elements being comprised of a first chain element including the first metal of the anionic component of the first salt and having a structure according to formula (V) and a second chain element including the second metal of the cationic component of the second salt and having a structure according to formula (VI)

where M¹ is molybdenum, tungsten, or vanadium; M² is selected from the group consisting of Fe, Ag, Co, Mn, Re, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, and Sn; and where Q is either sulfur or selenium. In this embodiment, the solid material contains at least one first chain element and at least one second chain element. At least a portion of the chain elements in the solid material are linked by bonds between the two sulfur atoms or the two selenium atoms of a chain element and the metal of an adjacent chain element.

In an embodiment of the present invention, the solid material separated from the aqueous mixture is comprised of monomeric units that repeat in the solid material to form a polymer, where a monomeric unit is comprised of a first metal of the anionic component of the first salt and a second metal of the cationic component from the second salt, bridged by, and bonded to, two sulfur atoms or two selenium atoms. The solid material may be comprised of units having the structure shown in formula VII:

where M¹ is molybdenum, tungsten, or vanadium; M² is selected from the group consisting of Fe, Ag, Co, Mn, Re, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, and Sn; Q is either sulfur or selenium; and x is at least 2, or at least 5, or at least 10.

Furthermore, the solid material may have a two-dimensional or a three-dimensional polymeric structure with alternating metal centers of the second metal of the cationic component from the second salt and the molybdenum, tungsten, or vanadium of the anionic component from the first salt bridged by two sulfur atoms or bridged by two selenium atoms. The two- and/or three-dimensional polymeric structure of a solid material produced hereby may have “holes” in its structure, in which a second metal of the cationic component from the second salt is missing as an alternating metal center. The two- and/or three-dimensional polymeric structure may contain a portion of the second metal of the cationic component of the second salt within interstices in the polymeric structure or in holes in the polymeric structure, where the portion of the second metal of the cationic component of the second salt located in the interstices or holes in the polymeric structure is not bonded with an anionic component from the first salt that forms a part of the polymeric structure and/or is not bonded with a sulfur atom or a selenium atom included in the polymeric structure.

The solid material separated from the aqueous mixture is typically at least partially crystalline, where the cystallinity of the solid material may be determined by x-ray powder diffraction. The solid material may be from 15% to 100% crystalline, or from 25% to 99% crystalline, of from 35% to 95% crystalline, or at least 20% crystalline, or at least 30% crystalline, or at least 40% crystalline, or at least 50% crystalline, or at least 60% crystalline, or at least 70% crystalline, or at least 75% crystalline. The solid material typically has a tetrahedral crystalline structure. The solid material also typically comprises alternating M^(I)S₄ and M^(II)S₄ tetrahedral formations or alternating M¹Se₄ and M²Se₄ tetrahedral formations, where each tetrahedral formation shares two sulfur atoms or two selenium atoms with an adjacent tetrahedral formation, and where M^(I) is the metal of the anionic component of the first salt and M^(II) is the metal of the cationic component of the second salt.

The solid material separated from the aqueous mixture typically comprises at most 0.1 wt. %, or at most 0.05 wt. %, or at most 0.01 wt. % oxygen. The oxygen content of the solid material may be determined by neutron activation, for example, in accordance with ASTM Method E385. In a preferred embodiment, oxygen is not detectable in the solid material. Oxygen is undesirable in the solid material when the solid material is to be used as a catalyst for hydrocracking a disadvantaged crude oil. The catalytic activity of the solid material as a hydrocracking catalyst is, in part, believed to be due to the availability of electrons from the solid material catalyst to stabilize cracked molecules in the crude oil. Due to its electronegativity, oxygen tends to reduce the availability of electrons from the solid material when it is present in the solid material in appreciable quantities. Also, as noted above, it is believed that inclusion of any significant quantity of oxygen in the solid material renders the solid material amorphous and not crystalline, which may substantially decrease the surface area of the solid material and reduce the effectiveness of the solid material as a catalyst.

The solid material separated from the aqueous mixture may contain at most 0.5 wt. %, or at most 0.1 wt. %, or at most 0.01 wt. % of the cationic component of the first salt. The cationic content of the first salt included in the solid material may be measured by x-ray fluorescence. The cationic component of the first salt may be an undesirable contaminant in the solid material. In an embodiment of the process of the present invention, the cationic component of the second salt is utilized in an atomic ratio to the metal of the anionic component of the first salt of greater than 1.5:1, or at least 1.6:1, or at least 2:1, or greater than 2:1 to ensure that the solid material contains less than 0.5 wt. % of the cationic component of the first salt. It is believed that the cationic component of the first salt may become included in the solid material if insufficient cationic component of the second salt is present to counterbalance the charge of the anionic component of the first salt upon formation of the solid material, therefore, sufficient cationic component of the second salt may be provided to reduce or eliminate the presence of the cationic component of the first salt in the solid material product.

The solid material separated from the aqueous mixture may contain less than 0.5 wt. % of ligands other than sulfur-containing ligands or selenium-containing ligands. Ligands, other than ligands formed from the sulfur or selenium provided by the first are not desirable in the solid material product since they may end-cap the compound formed by the combined cationic component of the second salt and the anionic component of the first salt, inhibiting addition of further repeating units of the cationic component of the second salt and the anionic component of the first salt to the end-capped compound. To inhibit the incorporation of such ligands into the solid material, the first salt and second salts are selected so that the cationic component of the first salt and the anionic component of the second salt are not capable of forming ligands with the cationic component of the second salt or the anionic component of the first salt or the solid material formed by repeating units thereof or with any component of the aqueous mixture.

The solid material separated from the aqueous mixture has a particle size distribution. The particle size distribution may have a median particle size and/or a mean particle size of from 50 nm to 50 μm, or from 75 nm to 10 μm, or from 100 nm to 1 μm, most preferably from 50 nm to 1 μm. In an embodiment of the invention, the solid material may have a particle size distribution with a mean and/or median particle size of from 50 nm up to 5 μm, or up to 1 μm, or up to 750 nm.

It is preferable that the solid material have a particle size distribution with a mean and/or median particle size of at least 50 nm so that the solid material may be utilized to hydrocrack and/or hydrotreat a heavy crude oil and be easily separated from the hydrocarbon feedstock, hydrocarbon product, and/or a byproduct stream. If the solid material has a mean and/or median particle size less than 50 nm, the solid material may be soluble in the hydrocarbon feedstock, product, and/or byproduct stream, rendering the solid material catalyst difficult to separate from hydrocarbon feedstock, product, and/or byproduct stream.

It is further preferable that the solid material have a particle size distribution having a mean and/or median particle size of at most 5 μm, more preferably of at most 1 μm, so that the solid material will have a relatively large surface area. A relatively large surface area is desirable when the solid material is used as a catalyst in hydrocracking and/or hydrotreating a hydrocarbon feedstock to provide high catalytic activity. The solid material particles may have a mean BET surface area of from 50 m²/g to 500 m²/g, or from 100 m²/g to 350 m²/g.

To facilitate a better understanding of the present invention, the following examples of certain aspects of some embodiments are given. In no way should the following examples be read to limit, or define, the scope of the invention.

EXAMPLE 1

A cobalt tetrathiomolybdate material, at least a portion of which had a structure according to formula (VIII), was produced by a process in accordance with the process of the present invention.

65.08 grams of (NH₄)₂MoS₄ were dissolved in 0.5 liters of deionized water under nitrogen and heated to 60° C. with stirring. A 240 milliter solution of 62.01 grams of Na₂CO₃.H₂O in deionized water was added dropwise to the heated stirred (NH₄)₂MoS₄ solution over 2 hours. The resulting solution was then stirred for 3 hours at 80° C. and then allowed to cool to ambient to produce a Na₂MoS₄ solution. Separately, 572.9 grams of CoSO₄ was dissolved in 1 liter of deionized water. 2 liters of water were heated to 80° C. under N₂, and the Na₂MoS₄ solution and the CoSO₄ solution were separately charged to the heated water under N₂ via pneumatic pump through 2″×0.02″ nozzles. A dark precipitate formed immediately, and the resulting slurry was stirred at 90° C. for 2 hours, then allowed to cool to 45° C. A solid material was separated from the slurry by continuous centrifuge at 12,000 gauss. The solid material was collected and washed until the liquid wash effluent had a neutral pH and a conductivity of 0.19 μS at 32.0° C. The washed solids were then dried under vacuum at 60° C. 75.5 grams of solid product were recovered.

Semi-Quantitative XRF of the recovered solid product measured, on a mass basis: 23.266% S; 31.917% Fe; and 18.826% Mo. The BET surface area of the solid material was measured to be 7.52 m²/gram and the solid material's single-point adsorption total pore volume was measured to be 0.017 cm³/gram. The solid material product had an adsorption average pore width of 89.6 Å.

EXAMPLE 2

An iron tetrathiomolybdate material, at least a portion of which had a structure according to formula (IX), was produced from ferrous iron by a process in accordance with the process of the present invention.

49.6 grams of Na₂CO₃.H₂O and 52.05 grams of (NH₄)₂MoS₄ were mixed under nitrogen in 1.5 liters of deionized water at 80° C. to form a Na₂MoS₄ solution. Separately, 194.6 grams of FeSO₄.7H₂O was mixed in 1 liter of deionized water. Approximately 200 mg of sodium dithionite was added to the iron solution to remove any oxygen. 2 liters of deionized water were heated separately to a temperature of 80° C., and the Na₂MoS₄ solution and the FeSO₄ solution were separately charged to the heated water under N₂ via pneumatic pump through 2″×0.02″ nozzles. A dark precipitate formed immediately, and the resulting slurry was stirred at 80° C. for 2.5 hours under nitrogen, then allowed to cool. A solid material was separated from the slurry by continuous centrifuge at 12,000 gauss. The solid material was collected and washed until the liquid wash effluent had a neutral pH and a conductivity of 0.36 μS at 26.0° C. The washed solids were then dried under vacuum at 55° C. 66.12 grams of solid product were recovered.

Semi-Quantitative XRF of the solid product measured, on a mass basis: 23.266% S; 31.917% Fe; and 18.826% Mo. The BET surface area of the solid product was measured to be 7.52 m²/gram and the solid product's single-point adsorption total pore volume was measured to be 0.017 cm³/gram. The solid product had an adsorption average pore width of 89.6 Å.

EXAMPLE 3

A nickel tetrathiomolybdate material, at least a portion of which had a structure according to formula (X), was produced by a process in accordance with the process of the present invention.

49.6 grams of Na₂CO₃.H₂O and 52.05 grams of (NH₄)₂MoS₄ were mixed under nitrogen in 1.5 liters of deionized water at 80° C. to form a Na₂MoS₄ solution. Separately, 489.1 grams of NiSO₄ were mixed in 1 liter of deionized water and heated to 80° C. 1 liter of deionized water were heated separately to a temperature of 71° C., and the Na₂MoS₄ solution and the NiSO₄ solution were separately charged to the heated water under N₂ via pneumatic pump through 2″×0.02″ nozzles. A dark precipitate formed immediately, and the resulting slurry was stirred at 80° C. for 2.5 hours under nitrogen, then allowed to cool. A solid material was separated from the slurry by continuous centrifuge at 8000 gauss. The solid material was collected and washed until the liquid wash effluent had a neutral pH and a conductivity of 50 μS at 24.3° C. The washed solids were then dried under vacuum at 55° C. 50.05 grams of solid product were recovered.

EXAMPLE 4

A zinc tetrathiomolybdate material was produced by a process in accordance with the process of the present invention. 42.4 grams of Na₂CO₃.H₂O and 52.07 grams of (NH₄)₂MoS₄ were mixed under nitrogen in 4 liters of deionized water at 75° C. to form a Na₂MoS₄ solution. Separately, 114.9 grams of ZnSO₄.H₂O were mixed in 4 liters of deionized water and heated to 75° C. 7 liters of deionized water were heated separately to a temperature of 87° C., and the Na₂MoS₄ solution and the ZnSO₄.H₂O solution were separately charged to the heated water under N₂ via pneumatic pump through 2″×0.02″ nozzles. A yellow ochre precipitate formed immediately, and the resulting slurry was stirred at 80° C. for 2.5 hours under nitrogen, then allowed to cool. A solid material was separated from the slurry by continuous centrifuge at 8000 gauss. The solid material was collected and washed until the liquid wash effluent had a pH of 4-5 and a conductivity of 55 μS at 26.1° C. The washed solids were then dried under vacuum at 55° C. 41.72 grams of solid product were recovered. Semi-Quantitative XRF of the solid product measured, on a mass basis: 7.953% Na; 21.311% S; 44.636% Zn; 14.458% Mo; and less than 0.005% Al, Si, Cl, Fe and Ni. The solid product was particulate and was found to have a multimodal particle size distribution between 0.05 μm to 878 μm with the highest particle volume distribution centered at 150 μm as determined by laser diffractometry using a Mastersizer S made my Malvern Instruments. The BET surface area of the solid product was measured to be 32.5 m²/gram and the solid product's single-point adsorption total pore volume was measured to be 0.061 cm³/gram. The solid product had a pore size distribution, where the median pore size diameter was determined to be 74.9 Angstroms.

EXAMPLE 5

A tin tetrathiomolybdate material was produced by a process in accordance with the process of the present invention. 42.4 grams of Na₂CO₃.H₂O and 52.05 grams of (NH₄)₂MoS₄ were mixed under nitrogen in 4 liters of deionized water at 80° C. to form a Na₂MoS₄ solution. Separately, 150.3 grams of tin (II) sulfate were mixed in 2.5 liters of deionized water and heated to 80° C. 3 liters of deionized water were heated separately to a temperature of 80° C., and the Na₂MoS₄ solution and the tin (II) sulfate solution were separately charged to the heated water under N₂ via pneumatic pump through 2″×0.02″ nozzles. A yellow ochre precipitate formed immediately, and the resulting slurry was stirred at 80° C. for 3 hours under nitrogen, then allowed to cool. A solid material was separated from the slurry by continuous centrifuge at 8000 gauss. The solid material was collected and washed until the liquid wash effluent had a pH of 5 and a conductivity of 0.71 μS at 22.4° C. The washed solids were then dried under vacuum at 55° C. 147.1 grams of solid product were recovered.

Semi-Quantitative XRF of the solid product measured, on a mass basis: 12.749% S; 61.775% Sn; 9.516% Mo; 0.998% Zn; and less than 0.049% Mg, Al, Si, Cu, and Pb. The BET surface area of the solid product was measured to be 114.8 m²/gram

The present invention is well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, as the present invention may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular illustrative embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the present invention. While compositions and methods are described in terms of “comprising,” “containing,” or “including” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components and steps. Whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range falling within the range is specifically disclosed. In particular, every range of values (of the form, “from a to b,” or, equivalently, “from a-b”) disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee. Moreover, the indefinite articles “a” or “an”, as used in the claims, are defined herein to mean one or more than one of the element that it introduces. 

What is claimed is:
 1. A method for producing a thiometallate or selenometallate material, comprising: mixing a first salt and a second salt in an aqueous mixture under anaerobic conditions, where, during mixing the aqueous mixture has a temperature of from 15° C. to 150° C., and wherein the first salt comprises a cationic component containing one or more metals selected from the group consisting of an alkali metal, an alkaline earth metal, and mixtures thereof and comprises an anionic component containing a first metal selected from the group consisting of Mo, W, and V where the anionic component is selected from the group consisting of MoS₄ ²⁻, MoSe₄ ²⁻, WS₄ ²⁻, WSe₄ ²⁻, VS₄ ³⁻, VSe₄ ³⁻ and mixtures thereof, and wherein the second salt comprises a cationic component comprising a second metal in any non-zero oxidation state selected from the group consisting of Fe, Ag, Co, Mn, Re, Ru, Rh, Pd, Ir, Pt, B, Al, Ce, La, Pr, Sm, Eu, Yb, Lu, Dy, Ni, Zn, Bi, Sn, and mixtures thereof, where the first and second salts are soluble in the aqueous mixture; separating a solid material from the aqueous mixture comprising a) the first metal of the anionic component of the first salt; and b) the second metal of the cationic component of the second salt and containing at most 0.5 wt.% of the cationic component of the first salt, wherein at least a portion of the solid material separated from the aqueous mixture has a structure according to a formula selected from the group consisting of formula (I), formula (II), formula (III), and formula (IV);

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, and Q is either sulfur or selenium;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃;

where M is either the first metal or the second metal, and at least one M is the first metal and at least one M is the second metal, Q is either sulfur or selenium, and X is selected from the group consisting of SO₄, PO₄, oxalate (C₂O₄), acetylacetonate, acetate, citrate, tartrate, Cl, Br, I, ClO₄, and NO₃.
 2. The method of claim 1 wherein the amount of the first salt and the amount of the second salt mixed in the aqueous mixture are selected to provide an atomic ratio of the second metal to the first metal of greater than 1.6:1.
 3. The method of claim 1 wherein the solid material separated from the aqueous mixture comprises at most 0.1 wt. % oxygen.
 4. The method of claim 1 wherein the amount of the first salt and the total volume of the aqueous mixture are selected to provide at most 0.2 moles of the anionic component from the first salt per liter of the total volume of the aqueous mixture, and where the amount of the second salt and the total volume of the aqueous mixture are selected to provide at most 1 mole of the cationic component of the second salt per liter of the total volume of the aqueous mixture.
 5. The method of claim 1 wherein the first salt is contained in a first aqueous solution and the second salt is contained in a second aqueous solution, and the first salt and the second salt are mixed in the aqueous mixture by mixing the first aqueous solution and the second aqueous solution.
 6. The method of claim 5 wherein the first aqueous solution containing the first salt and the second aqueous solution containing the second salt are added to a third aqueous solution to form the aqueous mixture.
 7. The method of claim 6 wherein the volume ratio of the third aqueous solution to the first aqueous solution is from 0.5:1 to 50:1 where the first aqueous solution contains at most 0.8 moles per liter of the first salt and the volume ratio of the third aqueous solution to the second aqueous solution is from 0.5:1 to 50:1 where the second aqueous solution contains at most 3 moles per liter of the second salt.
 8. The method of claim 6 where the first aqueous solution and the second aqueous solution are added to the third aqueous solution and mixed in the third aqueous solution such that the instantaneous concentration of the first salt in the aqueous mixture is at most 0.05 moles per liter and such that the instantaneous concentration of the second salt in the aqueous mixture is at most 0.05 moles per liter.
 9. The method of claim 5 further comprising the step of forming the first aqueous solution containing the first salt by mixing a salt comprising an alkali metal carbonate or an alkaline earth metal carbonate and an aqueous solution containing a salt selected from the group consisting of (NH₄)₂MoS₄, (NH₄)₂MoSe₄, (NH₄)₂WS₄, (NH₄)₂WSe₄, (NH₄)₃VS₄, (NH₄)₃VSe₄ and mixtures thereof at a temperature of from 50° C. to 150° C. under anaerobic conditions, where ammonia gas and carbon dioxide are evolved and degassed during mixing the salt comprising the alkali metal carbonate or alkaline earth metal carbonante and the aqueous solution containing the salt selected from the group consisting of (NH₄)₂MoS₄, (NH₄)₂MoSe₄, (NH₄)₂WS₄, (NH₄)₂WSe₄, (NH₄)₃VS₄, (NH₄)₃VSe₄ and mixtures thereof.
 10. The method of claim 1 wherein the solid material separated from the aqueous mixture is particulate and has a particle size distribution, where the mean particle size or the median particle size of the particle size distribution of the solid material is from 50 nm to 10 μm.
 11. The method of claim 1 wherein the solid material separated from the aqueous mixture is particulate where the particles have an average BET surface area of from 50 m²/g to 500 m²/g.
 12. The method of claim 1 wherein the solid material is at least 20% crystalline.
 13. The method of claim 1 wherein the aqueous mixture contains more than 0 vol. % but less than 50 vol. % of an organic solvent containing from 1 to 5 carbons and selected from the group consisting of an alcohol, a diol, an aldehyde, a ketone, an amine, an amide, a furan, an ether, acetonitrile, and mixtures thereof where the first salt and the second salt are soluble in the aqueous mixture.
 14. The method of claim 1 wherein the solid material comprises alternating M¹S₄ and M²S₄ tetrahedral formations, where each tetrahedral formation shares two sulfur atoms with an adjacent tetrahedral formation, and where M¹ is the first metal and M² is the second metal.
 15. The method of claim 1 wherein the solid material separated from the aqueous mixture is comprised of alternating atoms of the first metal and the second metal bonded to and linked by two sulfur atoms.
 16. The method of claim 1 wherein the solid material separated from the aqueous mixture is comprised of at least three linked chain elements, the chain elements being comprised of a first chain element including the first metal and having a structure according to formula (V) and a second chain element including the second metal and having a structure according to formula (VI)

where M¹ is the first metal, where M² is the second metal, and where Q is either sulfur or selenium; where the solid material contains at least one first chain element and at least one second chain element, and where at least a portion of the chain elements in the solid material are linked by bonds between two sulfur atoms or two selenium atoms of a chain element and the metal of an adjacent chain element.
 17. The method of claim 1 wherein the solid material is comprised of a plurality of anionic components from the first salt and a plurality of cationic components from the second salt where the anionic components from the first salt are bonded with at least a portion of the cationic components from the second salt in two or more repeating units.
 18. The method of claim 1 wherein the solid material separated from the aqueous mixture is comprised of monomeric units that repeat in the solid material so that the solid material product is a polymer formed of the repeating monomeric units, where a monomeric unit is comprised of the first metal and the second metal bridged by, and bonded to, two sulfur atoms or two selenium atoms, the polymer having the structure of formula (VII):

where M¹ is the first metal, M² is the second metal, Q is either sulfur or selenium, and x is at least
 2. 19. The method of claim 1 wherein the solid material separated from the aqueous mixture contains less than 0.5 wt. % of ligands other than sulfur or selenium containing ligands.
 20. The method of claim 1 further comprising the step of washing the solid material with water subsequent to separation of the solid material from the aqueous mixture.
 21. The method of claim 1 further comprising the step of drying the separated solid material. 